Necessary conditions for T/C80/20 Poly cotton woven interlinings with HDPE coating for shirts and fabric bonding
T/C80/20 Poly cotton woven interlinings with HDPE coating for shirts is an important part of clothing, T/C80/20 Poly cotton woven interlinings with HDPE coating for shirts after processing and fabric bonding will affect the adhesion due to different materials , generally meet the following three conditions to solve the bonding problem:
1. Bonding machine: There are generally two types of bonding machines: roller type and flat type.
2. Bonding conditions: bonding conditions include bonding temperature, pressing time and pressure. In a certain range, the three elements interact with each other to a certain extent. When the temperature increases and the pressure increases, the pressing time can be relatively shortened, and vice versa. If the temperature is too high and the pressing time is too long, it is easy to damage the performance and color of the fabric, and it is also easy to produce glue penetration.
3. Selection of bonding conditions: Before mass production, the bonding conditions must be repeatedly tested to determine the optimal process conditions (when testing small samples, the interlining supplier should provide bonding conditions for reference).
T/C80/20 Poly cotton woven interlinings with HDPE coating for shirts after bonding with the fabric. Peel it off, if the hot melt adhesive is evenly distributed on the lining and fabric, the bonding conditions are appropriate, otherwise the test should be re-tested. After bonding, the cloth surface should be flat, without wrinkles, bubbles, and glue. After bonding, the peel strength, dry cleaning and water washing performance tests should be carried out, and the test results should meet the production requirements. The effect of bonding should meet the style and characteristic requirements of clothing.